eNauka >  Results >  Hydrogen embrittlement effects on remaining life and fatigue crack growth rate in API 5L X52 steel pipelines under cyclic pressure loading
Title: Hydrogen embrittlement effects on remaining life and fatigue crack growth rate in API 5L X52 steel pipelines under cyclic pressure loading
Authors: Bouledroua, Omar; Zelmati, Djamel; Hafsi, Zahreddine; Djukic, Milos B  
Issue Date: 2024
Publication: ENGINEERING FAILURE ANALYSIS
ISSN: 1350-6307 Engineering Failure Analysis Search Idenfier
Type: Article
Collation: vol. 166 str. 108917-108917
DOI: 10.1016/j.engfailanal.2024.108917
WoS-ID: 001329761300001
Scopus-ID: 2-s2.0-85205256696
URI: https://enauka.gov.rs/handle/123456789/942475
Metadata source: (Preuzeto iz Nasi u WoS)