Influence of hydrogen-enhanced plasticity and decohesion mechanisms of hydrogen embrittlement on the fracture resistance of steel
| Назив: | Influence of hydrogen-enhanced plasticity and decohesion mechanisms of hydrogen embrittlement on the fracture resistance of steel | Аутори: | Wasim, Muhammad; Đukić, Miloš   ; Tuan Duc Ngo |
Година: | 2021 | Публикација: | Engineering Failure Analysis | ISSN: | 1350-6307 Engineering Failure Analysis Претражи идентификатор |
Издавач: | Pergamon-Elsevier Science Ltd, Oxford | Тип резултата: | Научни чланак | Колација: | vol. 123 str. 105312-105312 | DOI: | 10.1016/j.engfailanal.2021.105312 | WoS-ID: | 000633003700002 | Scopus-ID: | 2-s2.0-85101859308 | URI: | https://machinery.mas.bg.ac.rs/handle/123456789/3499 https://enauka.gov.rs/handle/123456789/573566 |
Пројекат: | The authors gratefully acknowledge RMIT University's testing facilities used for performing toughness testing and RMMF for carrying out fractography. | М-категорија: | 21M21 - Водећи међународни часопис категорије M21 |