eNauka >  Rezultati >  Influence of hydrogen-enhanced plasticity and decohesion mechanisms of hydrogen embrittlement on the fracture resistance of steel
Naziv: Influence of hydrogen-enhanced plasticity and decohesion mechanisms of hydrogen embrittlement on the fracture resistance of steel
Autori: Wasim, Muhammad; Đukić, Miloš  ; Tuan Duc Ngo
Godina: 2021
Publikacija: Engineering Failure Analysis
ISSN: 1350-6307 Engineering Failure Analysis Pretraži identifikator
Izdavač: Pergamon-Elsevier Science Ltd, Oxford
Tip rezultata: Naučni članak
Kolacija: vol. 123 str. 105312-105312
DOI: 10.1016/j.engfailanal.2021.105312
WoS-ID: 000633003700002
Scopus-ID: 2-s2.0-85101859308
URI: https://machinery.mas.bg.ac.rs/handle/123456789/3499
https://enauka.gov.rs/handle/123456789/573566
Projekat: The authors gratefully acknowledge RMIT University's testing facilities used for performing toughness testing and RMMF for carrying out fractography.
M-kategorija: 
21M21 - Vodeći međunarodni časopis kategorije M21

212
SCOPUSTM
193
WEB OF SCIENCETM
Alt metrika
Dimensions
Unpaywall

Rezultati na eNauka su zaštićeni autorskim pravima i sva prava su zadržana, osim ako nije drugačije naznačeno.